Abstract
Membranes, due to their smaller footprint and potentially lower energy consumption than the amine process, offer a promising route for post-combustion CO2 capture. Zeolite Y based inorganic selective layers offer a favorable combination of CO2 permeance and CO2/N2 selectivity, membrane properties crucial to the economics. For economic viability on large scale, we propose to use flexible and scalable polymer supports for inorganic selective layers. The work described in this paper developed a detailed protocol for depositing thin zeolite Y seed layers on polymer supports, the first step in the synthesis of a polycrystalline zeolite Y membrane. We also studied the effects of support surface morphology (pore size and surface porosity) on the quality of deposition and identified favorable supports for the deposition. Two different zeolite Y particles with nominal sizes of 200nm and 40nm were investigated. To obtain a complete coverage of zeolite particles on the support surface with minimum defects and in a reproducible manner, a vacuum-assisted dip-coating technique was developed. Images obtained using both digital camera and optical microscope showed the presence of color patterns on the deposited surface which suggested that the coverage was complete. Electron microscopy revealed that the particle packing was dense with some drying cracks. Layer thickness with the larger zeolite Y particles was close to 1μm while that with the smaller particles was reduced to less than 0.5μm. In order to reduce drying cracks for layers with smaller zeolite Y particles, thickness was reduced by lowering the dispersion concentration. Transport measurement was used as an additional technique to characterize these layers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.