Abstract
Bulk samples with high mechanical strength reaching 1000 MPa were obtained from electroexplosive Fe-Fe3O4 nanoparticles containing 81 wt. % Fe. Maximum strength is achieved by consolidation of the nanoparticles by isostatic pressing followed by vacuum sintering at 700 °C. A further increase in the sintering temperature leads to the formation of large pores with a size of up to 5 μm and an intense interaction of Fe and Fe3O4 with the formation of FeO leading to the embrittlement of the samples and a decrease in their strength. The degradation rate of Fe- Fe3O4 samples in NaCl (0.9% wt.) and Hank's solution is 7 times higher than that of samples obtained by sintering an electroexplosive Fe nanopowder under the same conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.