Abstract
Double-sides of aluminum sheet were anodized; at first, one side (front-side) of aluminum sheet was anodized, and the pores were filled with nickel using electroplating technique. Next, the other side (back side) of aluminum sheet was anodized. After formation of electrodes on both sides of anodic porous alumina, the current–voltage characteristics were examined, and reversible change in the resistance between metallic and insulating states was measured during mono-polar operation. This switching behavior could be measured for the sample with the depth of backside pores of about 100μm. The bias voltage, at which the resistance state changed into the lower-resistance state from the higher-resistance state, decreased with decreasing the depth of backside pores, and the bias voltage was about 1V in the case of the backside pores of about 10μm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.