Abstract
Monolayer polystyrene spheres (∼400 nm) array templates were assembled orderly on clean glass substrates by dip-drawing method from emulsion of PS and porous TiO2 thin films were prepared by using sol-dipping template method to fill TiO2 sol into the interstices among the close-packed PS templates and then annealing to remove the PS templates. The effects of TiO2 precursor sol concentration and dipping time in sol on the porous structure of the thin films were studied. The results showed pore size of the ordered TiO2 porous thin film depended mainly on PS size and partly on TiO2 sol concentration. The shrinkage of pore diameter was about 10% for 0.2 M and 20% for 0.4 M TiO2 sol concentrations. X-ray diffraction (XRD) spectra indicated the porous thin film was anatase structure. The transmittance spectrum showed that optical transmittance of the porous thin film kept above 70% beyond the wavelength of 430 nm. Optical band-gap of the porous TiO2 thin film (fired at 550∘;C) was 3.12 eV.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.