Abstract
Foam glass was prepared which using iron tailings and waste glass with SiC powders as foaming agent. The influence of the foam temperature on the bulk density, porosity, water absorption and compressive strength was studied. The results show that foam glass with higher iron tailings content of 24.5wt% could be prepared at about 830°C for 30min. Some of the reactions inside the iron tailings are responsible for the foaming mechanisms. When the foam temperature was 830°C, the bulk density and flexural strength reached a minimum value of 0.224g/cm3 and 0.53MPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.