Abstract
A superhydrophobic fabric coating with hierarchical structure was fabricated by a dip coating, in which dodecyltrimethoxysilane (DTMS)‐modified alumina (Al2O3) was used as modifier and polydimethylsiloxane (PDMS) as additive. The effects of the amounts of Al2O3 nano‐sized particles and PDMS on the water contact angle (WCA) and the sliding angle (SA) of the as‐prepared fabrics coating samples were studied. The surface morphology of the as‐prepared samples was characterized by SEM, and the abrasion resistance and chemical resistance experiments were performed by abrasion resistance test, tape tear test, and chemical soaking test. The results show that WCA and SA of the superhydrophobic fabrics coating are 158° and 6°, respectively. With the increasing addition of PDMS, the abrasion resistance of hydrophobic fabrics coating is improved. The WCA value of the as‐prepared fabrics coating is still >150° after five abrasion cycles. The obtained fabrics exhibit excellent superhydrophobicity and oleophilicity due to the hydrophobic modification of DTMS for Al2O3 nano‐sized particles. And the separation efficiency of the as‐prepared superhydrophobic fabrics coating for n‐dodecane and water system can reach 99.98%. POLYM. COMPOS., 2018. © 2018 Society of Plastics Engineers
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.