Fabrication of Diamond Nanopit arrays by Room-temperature Curing Nanoimprint Lithography Using Glass-like Carbon Molds

Abstract

ABSTRACTWe have proposed the use of glass-like carbon (GC), as mold material because the 27-maximum etching selectivity of polysiloxane film against GC, which was approximately sixtimes larger than that of polysiloxane film against chemical vapor deposited (CVD) diamond film. We have investigated the fabrication of diamond nanopit arrays by room-temperature curing nanoimprint lithography (RTC-NIL) using GC mold, as applications to the emitter and the micro-gear. The polysiloxane has in the state of sticky liquid at room-temperature and negative-exposure characteristic. Therefore, the polysiloxane was used as RTC-imprint resist material, and also used as electron beam (EB) resist (oxide mask) material in EB lithography. We have fabricated the cylindrical GC nanodot mold with 500 nm-diameter, 600 nm-height and 2 μm-pitch. We carried out RTC-NIL using GC mold under the following optimum conditions: time from spin-coating to imprint of 1 min, imprinting pressure of 0.5 MPa and imprinting time of 5min. Then, we have processed the diamond film with an electron cyclotron resonance (ECR) oxygen ion shower. We have fabricated diamond nanopit array with 250 nm-depth and 500 nm-diameter. The diameter of diamond nanopit pattern was in good agreement with that of GC mold. Moreover, the depth of the diamond nanopit patterns fabricated by RTC-NIL using cylindrical GC mold was three times larger than that using conical diamond mold.