Diamond Nanopit Arrays Fabricated by Room-Temperature Nanoimprinting using Diamond Molds

Abstract

ABSTRACTWe have investigated the nanopatterning of chemical vapor deposited (CVD) diamond films in room-temperature nanoimprint lithography (RT-NIL), using a diamond nanodot mold. We have proposed the use of polysiloxane as an electron beam (EB) mask and RT-imprint resist materials. The diamond molds of cylinder dot using the RT-NIL process were fabricated with polysiloxane oxide mask in EB lithography technology. The dot in minimum diameter is 500 nm. The pitch between the dots is 2 μm, and dot has a height of about 600 nm. It was found that the optimum imprinting conditions for the RT-NIL : time from spin-coating to imprinting t1 of 1 min , pressure time t2 of 5 min, imprinting pressure P of 0.5 MPa. The imprint depth obtained after the press under their conditions was 500 nm. We carried out the RT-NIL process for the fabrication of diamond nanopit arrays, using the diamond nanodot molds that we developed. The resulting diamond nanopit arrays with 500 nm-diameter and 200 nm-depth after the electron cyclotron resonance (ECR) oxygen ion beam etching were fabricated. The diameter of diamond nanopit arrays was in good agreement with that of the diamond nanodot mold.