Permutite incorporating CdSe in mesopores has been prepared with a simple route. Firstly, mercaptosuccinic acid-capped CdSe quantum dots (QDs) were prepared in aqueous solution by using SeO2 as selenium source and NaBH as reductant. Secondly, the commercial permutite was treated with acetic acid to induce a partial dealumnization, which can introduce a large number of intracrystal mesopores, and the CdSe QDs were successfully incorporated in the mesopores with the wet impregnation method. Photoluminescence spectra, X-ray diffraction and scanning electron microscopy were used for the characterization of samples. The spectra analyses results showed that the illuminant colour of QDs/permutite powder was similar to the corresponding QDs colloid. X-ray diffraction measurements indicated that the (1 0 1) diffraction peak at 2𝜃 = 27° for QDs/permutite powder was the same as the raw permutite, and the energy-dispersive X-ray spectra demonstrated that Cd and Se elements existed in the CdSe QDs/permutite powder.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.