Abstract
Yttria–doped ceria powder was prepared from oxalate precursors. The oxalate coprecipitation bath parameters were closely monitored and found to influence the sintering behavior of the subsequently obtained oxide powders strongly. The use of concentrated (Ce,Y) metal nitrate solutions and dilute neutralized oxalic acid for coprecipitation were identified as the most–important parameters. Following calcination at 700°C, compacts of such powders were sintered to high density (98%) at 1400°C (4 h). Ball milling of the powder further reduced the sintering temperature. Dry milling, for tape–casting applications of the powder in particular, was more effective than wet milling. Tape–cast membranes were fired at 1400°C (2 h), with resulting densities of 98%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.