Fabrication and properties of 3D printed zirconia scaffold coated with calcium silicate/hydroxyapatite

Abstract

The scaffold of bone repair needs a variety of material combinations to meet its intended performance; a typical single material such as zirconia has excellent mechanical properties, while hydroxyapatite and calcium silicate are bioactive materials with different degradation rates. In this paper, porous zirconia scaffolds were fabricated using 3D printing technology. The surface of the scaffold was coated by dipping with different contents of calcium silicate and hydroxyapatite to improve the biological activity and mechanical properties. Mechanical tests show that the coating material can effectively fill the pores of the porous scaffold, increasing its compressive strength by an average of 55%. The simulated body fluid (SBF) test showed that the higher calcium silicate in the coating increased the degradation rate. Cell experiments showed that the coated scaffolds exhibited good cytocompatibility and were beneficial to the proliferation and differentiation of cells. In conclusion, coated scaffolds have potential applications in the field of bone repair.