Fabrication and evaluation of piezoelectric drive type 2-axis tilt control device using epitaxial PZT thin film

Abstract

Piezoelectric drive type 2-axis tilt control device using epitaxial Pb(Zr <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.52</sub> , Ti <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.48</sub> )O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> (PZT) thin film on epitaxial γ-Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> /Si substrate have been fabricated. A 500 nm-thick epitaxial PZT(111) thin film was sol-gel deposited on epitaxial SrRuO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> (111)/Pt(111)/ γ-Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> (111)/Si(1 11) substrates, and hollow structure under actuate area was formed by XeF <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> gas etching. The fabricated device showed polarization-electric field (P-E) hysteresis loop of piezoelectric PZT thin film and the deflection. Therefore, the realization of piezoelectric drive type deformable mirrors (DMs) using epitaxial PZT thin film can be expected.