Abstract
The conducting metal oxide (ZnO, Cu2O) films were used for fabrication of p-n heterojunction by rf sputtering and electrodeposition techniques respectively. The as synthesized films were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), UV spectroscopy and electrical techniques. The electrical properties of the p-Cu2O/n-ZnO heterojunction were examined using the current-voltage measurements. The current-voltage (I-V) result showed that potential barrier was higher than the turn-on voltage, which was attributed to the presence of the interface defect states. The PN junction parameters such as ideality factor, barrier height, and series resistance were determined using conventional forward bias current-voltage characteristics. The annealing of Cu2O increase the crystallinity size and which enhance the photo current from 1.6 mA/cm2 to 3.7 mA/cm2. The annealing of respective film resulted in a decrease of these parameters with an increase in efficiency of solar cell from 0.14% to 0.3% at 350 degrees C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.