Abstract
In the present work, the isothermal section at 1200 °C of the V–Cr–Si phase diagram was experimentally studied. The samples were prepared by arc melting and characterized using scanning electron microscopy/energy-dispersive spectroscopy and electron probe microanalyzer. The continuous solution phases (Cr,V)3Si, (Cr,V)5Si3 and (Cr,V)Si2 were confirmed. The solubilities of Cr in V6Si5 and of V in CrSi have been measured. A ternary phase (Cr,V)11Si8 was observed and its homogeneity range, which is at constant Si ratio, was determined at 1200 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.