Abstract
This paper outlines the TIG welding process without using active flux for 4[Formula: see text]mm-thick plates of duplex stainless steel (DSS 2205) and austenitic stainless steel (SS 304L). It also provides the properties and behavior analysis of weldments. Complete penetration is achieved with multi-pass welding. The microstructure is examined using an optical microscope (OM) and a scanning electron microscope (SEM). It was used to report on the differences between the unpolished zone and the heat-affected zone (HAZ) in weldments. A Vickers hardness tester (HV scale 10) was used to assess the weldment’s hardness. Tensile and bend failure were among the mechanical properties exhibited by the parent metals of DSS2205, SS304L, and dissimilar junctions. The findings demonstrated shallow gaps in the surface area and a greater ultimate tensile strength of 600[Formula: see text]MPa for DSS similar welding. However, compared to other similar weldments, dissimilar weldments exhibit superior performance in bending conditions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.