Abstract
A strain isolation pad is a critical connection mechanism that enables deformation coordination between the rigid thermal insulation tile and the primary structure in the thermal protection system of a reusable hypersonic vehicle. An experimental investigation has been conducted to determine the static, loading–unloading, and high-cycle fatigue (HCF) responses of the SIP with 0.2 mm adhesive under through-thickness tension at room temperature. The contributions of the rigid thermal insulation tile and metallic substructure have not been considered so far. The results indicate that the tensile behavior of the SIP joint is highly nonlinear. The static and fatigue tensile failures both initiate from the corner close to the adhesive/SIP interface due to the stress concentration and the edge effect. The uniform breakage of the aramid fiber can be seen on the cross-section. A novel method is proposed to quantify the residual strain due to the short-time ratcheting effect of the SIP joint in the initial loading–unloading tensile response. As the number of fatigue cycles increases, the thickness of the SIP joint continues to increase until failure. An explicit expression associated with the growth of SIP joint thickness, fatigue cycle number, and peak cyclic stress is established. The turning point of the thickness growth rate with the fatigue cycle number is proposed as a new fatigue failure index for the SIP joint under tensile fatigue, and a fatigue life prediction model is developed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.