Abstract
Due to high hole mobility, p-GaSb is an attractive III-V semiconducting material for high performance p-channel metal-oxide semiconductor field effect transistor (p-MOSFET). For that growth of undoped and Ni doped GaSb bulk crystal by thermal vertical directional solidification technique has been reported in this paper. X-ray diffraction (XRD) analysis confirms that the both grown compounds are polycrystalline in nature which have been supported by scanning electron microscope (SEM) image. The carrier charge density and mobility were measured by Hall Effect measurement in the temperature range 78K and 300K. From the sign of Hall co-efficient the both grown materials were confirmed p-type. The Current-Voltage (I-V) characteristic was studied for both the sample i.e. experimentally grown and also simulated using TCAD at 78K and 300K. The temperature dependence of the hole mobility were also investigated by TCAD tool using the models Auger recombination, Shockley-Read-Hall (SRH) and Band-gap narrowing (BGN). Comparison of experimental and simulated temperature dependencies of mobility shows good agreement, while their differences at some points suggests the contribution of compensating impurities.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have