Abstract
In our previous study, we investigated ammonia-free phosphate-bonded investments using Mg (H2PO4)2 powder. The purpose of the present study was to attempt usage of 50 wt% Mg (H2PO4)2 solution instead of powder. Magnesium oxide (MgO) was prepared as a binder and cristobalite was selected as a refractory. After arranging six kinds of experimental investments (A-F) with different cristobalite/MgO ratios, the fundamental properties of the dental investments were examined. The properties of the molds were influenced by the amount of MgO. Decreases in MgO showed lower mold strengths, longer setting time and larger setting expansion. According to XRD analysis, the peaks of MgH(PO4)3 x 3H2O newly formed, cristobalite and MgO were detected in the A set, but MgO peaks in F set were reduced. On the other hand, the surface of F was entirely covered by phosphorus. From these results, it was found that the usage of Mg(H2PO4)2 solution was possible for ammonia-free investments.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.