Experiment of enhancing critical current and reducing ac loss in pancake coil comprised of Ni-coated Bi-2223/Ag tape

Abstract

An approach of realizing high performance HTS coil comprised of ferromagnetic material-coated BSCCO tape is proposed. The concept of influencing critical current and ac loss is based on the magnetic shielding effect resulting in redirection of self-field flux-lines. In the previous article, ac performance of Ni-coated tape was demonstrated where the Ni-coating was introduced at the edge-regime of the finished tape in order to redirect the perpendicular component of self-field lines. In order to investigate the shielding effect on ac performance in HTS coil, a two-turn pancake coil comprised of Ni-coated Bi-2223/Ag tape is demonstrated in the present article. About 6.4% of critical current was enhanced and 30% of transport current ac loss was reduced by means of 40 μm thick and 0.3 mm long (from the edge toward center of the tape) Ni-coating. This result suggests that additional ferromagnetic loss could be compensated well by the shielding effect of the partial Ni-coating. The degree of enhancement in critical current as well as ferromagnetic impact on ac losses depend on the volume and geometry of ferromagnetic coating introduced. Therefore, it is very important to control the parameter of ferromagnetic coating of the tape in order to balance the critical current and ac loss for optimum coil performance.