Abstract
The heat capacity of 9.70 and 11.35 mol% yttria stabilized zirconia ((ZrO2)1−x(Y2O3)x; x=0.0970, 0.1135) was measured by adiabatic calorimetry between 13 and 300 K, and some thermodynamic functions were calculated and given in a table. A large excess heat capacity extending from the lowest temperature to room temperature with a broad maximum at about 75 K was found in comparison with the heat capacity calculated from those of pure zirconia and yttria on the basis of simple additivity rule. The shape of the excess heat capacity is very similar to the Schottky anomaly, which may be attributed to a softening of lattice vibration. The amount of the excess heat capacity decreased with increasing yttria doping, while the maximum temperature did not vary. The relationships among the excess heat capacity, defect structure and interatomic force constants, and also the role of oxygen vacancy were discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.