Abstract
The porosity and its effect on critical current density J/sub c/ of Ag-clad (Bi,Pb)/sub 2/Sr/sub 2/Ca/sub 2/Cu/sub 3/O/sub x/ (Bi-2223) tapes throughout important steps in their thermomechanical treatment was investigated by using mass density measurement, microstructural observation, and superconducting property characterization. The relative mass density of the final filament for 19 filament tape was less than 75%, even though the J/sub c/ is /spl sim/50 kA/cm/sup 2/ (77 K, 0 T). The mass density in monofilaments reached 90%, because retrograde densification during the first heat treatment (HT1) was less or even absent. Well textured Bi-2223 grain growth could result in a significant densification during the first HT in the monofilament composite. Our results hint at considerable variability in this important property of Bi-2223 tape.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.