Abstract
Single-phase polycrystalline La1.5Ca0.5CoMnO6 double perovskite nanoparticles (∼25nm) have been synthesized by chemical sol-gel method. We report here the structural, magnetic and transport properties using X-ray diffraction, dc magnetization, ac susceptibility, exchange bias and dc resistivity measurements. The Rietveld refinement of X-ray diffraction pattern reveals that the La1.5Ca0.5CoMnO6 (LCCMO) system crystallizes in orthorhombic structure with pbnm space group. Mn and Co ions are not completely ordered on the B sites due to the presence of about 30% antisite-disorder in the system. The ordering of Co2+ and Mn4+ gives rise to the ferromagnetism below 145K. A spin glass like ground state has also been observed near 37.6(4)K, arising mainly due to the presence of competing magnetic interactions and antisite-disorder in the LCCMO nanoparticles. The frequency dependence peak shift of the Ac-susceptibility peak in the glassy state follows the critical slowing down model. The observed memory effect in ac susceptibility data reveals the existence of interacting clusters in a competing magnetic interactions state. The presence of noticeable exchange bias effect can be best explained on the basis of uncompensated interface (ferromagnetic/spin-glass) spins of antisite-disordered LCCMO system. This anti-site disordered nanocompound exhibits semiconducting behavior with variable range hopping kind of electronic conduction mechanism in the temperature range of 200–300K. We have also observed large negative magnetoresistance (−30% at 100K and 60kOe) mainly due to the spin-polarized transport across the grain boundaries.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call