Abstract

TEM specimens of a LaAlO(3)/SrTiO(3) multilayer are prepared by FIB with internal lift out. Using a Ga(+1) beam of 5 kV, a final cleaning step yielding top, top-angle, side, and bottom-angle cleaning is performed. Different cleaning procedures, which can be easily implemented in a dual beam FIB system, are described and compared; all cleaning types produce thin lamellae, useful for HRTEM and HAADF-STEM work up to atomic resolution. However, the top cleaned lamellae are strongly affected by the curtain effect. Top-angle cleaned specimens show an amorphous layer of around 5 nm at the specimen surfaces, due to damage and redeposition. Furthermore, it is observed that the LaAlO(3) layers are preferentially destroyed and transformed into amorphous material, during the thinning process.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.