Abstract
The investment casting process is an economic production method for engineering components in TiAl-based alloys and offers the benefits of a near net-shaped component with a good surface finish. An investigation was undertaken to develop three new face coat systems based on yttria, but with better sintering properties. These face coat systems were mainly based on an yttria-alumina-zirconia system (Y2O3-0.5 wt pct Al2O3-0.5 wt pct ZrO2), an yttria-fluoride system (Y2O3-0.15 wt pct YF3), and an yttria-boride system (Y2O3-0.15 wt pct B2O3). After sintering, the chemical inertness of the face coat was first tested and analyzed using a sessile drop test through the metal wetting behavioral change for each face coat surface. Then, the interactions between the shell and metal were studied by centrifugal investment casting TiAl bars. Although the sintering aids in yttria can decrease the chemical inertness of the face coat, the thickness of the interaction layer in the casting was less than 10 μm; therefore, these face coats still can be possible face coat materials for investment casting TiAl alloys.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.