Abstract
The current study was conducted to assess the effects of various surface treatments on the implant surface. A total of 45 dental implants measuring 16 mm in length and 5 mm in diameter were used, along with the appropriate abutments. Depending on the surface treatment used, the samples were randomly split into three groups, with 15 implants in each group: Group 1: Control, Group 2: UV light-treated, Group 3: Sandblasted and acid-etched (SLA)-treated. After surface treatment, a scanning electron microscope (SEM) was used to assess the test samples' surface properties. All sample images were captured using a 3000× magnification. After all three groups' surfaces were treated, the surface roughness was measured using a digital optical profilometer with a stylus speed of 0.5 mm/s that was connected to computer software. The maximum surface roughness was found in the group treated with SLA (0.714 ± 0.12), followed by the group treated with UV light (0.692 ± 0.09) and the control group (0.516 ± 0.12). There was a significant difference found between different surface treatment methods. The present study concluded that the group that received the SLA treatment had the highest surface roughness when compared to the UV light and control groups.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.