Abstract
Ferritic stainless steel (SS) interconnect used for intermediate temperature solid oxide fuel cell has issues associated with the growth of oxide scale on the surface and evaporation of chromium species to the cathode leading to increase in polarization resistance and hence, overall cell resistance. Protective coating is essentially applied over the SS surface to restrict the above phenomena. In the present investigation, strontium doped lanthanum manganese chromite (LSCM) of composition La0.75Sr0.25Cr0.5Mn0.5O3 has been explored as a possible protective coating material on ferritic SS interconnect surface. For this application, fine LSCM powder was synthesized by solution polymerization method. Terpineol based slurry of LSCM was formulated and used for coating on ferritic SS surface by screen printing. LSCM coated ferritic SS was exposed to moist oxygen at 800 °C for 300 h and area specific resistance (ASR) of the coating was found to be as low as 2.0 mΩ cm2 after exposure. Microstructure of LSCM coating and the chromium oxide film was investigated using SEM and EDS. The results indicate that LSCM can form an effective protective coating on ferritic stainless steel for SOFC interconnect application.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.