Abstract
In this study, electrical resistivity was related to the fundamental geotechnical properties of cement solidified/stabilized heavy metal–contaminated soils. Lead-contaminated soils were artificially prepared with various concentrations and treated by portland cement Type I at three content levels. The compacted cylindrical specimen was prepared with a diameter of 50 mm and height of 100 mm. The apparent electrical resistivity, electrical conductivity of pore fluid, unconfined compressive strength, and water contents were measured at different curing times. The result shows that the apparent electrical resistivity increases with the increase of curing time and the decrease of porosity and saturation degree as a result of cement hydration development. The effects of lead concentration, cement content, and curing time on the apparent electrical resistivity were discussed. The cementation index m was used to evaluate the cementation degree of cement-treated lead-contaminated soils. Lead pollutant at high concentrations could suppress or retard the hydration of solidified/stabilized soils. Electrical resistivity measurements can be used as a nondestructive method to evaluate the hydration development of solidified/stabilized lead-contaminated soils.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Hazardous, Toxic, and Radioactive Waste
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.