Abstract
In this study Y2O3 thin films were etched with an inductively coupled plasma. The etch rate of Y2O3 and the selectivity of Y2O3 to YMnO3 were investigated by varying the Cl2/(Cl2+Ar) gas mixing ratio. The maximum etch rate of Y2O3 and the selectivity of Y2O3 to YMnO3 were 302 Å/min and 2.4, respectively, at a Cl2/(Cl2+Ar) gas mixing ratio of 0.2. Based on x-ray photoelectron spectroscopy analysis, it was concluded that the Y2O3 thin film was dominantly etched by Ar ion bombardment and was assisted by the chemical reaction of a Cl radical. This result was confirmed by secondary ion mass spectroscopy analysis with the presence of a Y–Cl bond at 124.4 (amu).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Vacuum Science & Technology A: Vacuum, Surfaces, and Films
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.