Abstract
Iron aluminide intermetallic coatings were prepared from Fe−Al/Cr3C2 cored wires using High Velocity Arc Spraying (HVAS) technology. Erosion and corrosion properties of HVAS sprayed Fe−Al/Cr3C2 coatings were investigated. Results show that the erosion at impingement angle of 30° is more than that of 90°. The erosion resistance of coatings was enhanced with the increase of temperature. Coatings had a better erosion resistance than substrates. The erosion changed from ductile behaviors to brittle behaviors above 450°C. At high temperature, the erosion resistances were superior to those at low temperature and room temperature. Coatings had much higher corrosion properties than substrates. The temperature had a little effect on the corrosion resistance of coatings; The corrosion losing of coatings increased slowly with the increase of corrosion time. The HVAS-sprayed Fe−Al/Cr3C2 coatings exhibited a high bond strength and hardness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.