Abstract
Heat treatments after cold rolling for TiNiFe shape-memory alloys have been compared. After EBSD analysis and as calculated by the Avrami model and Arrhenius equation, the relationship between the heat-treatment temperature and manufacturing time of TiNiFe alloys is established. Through calculation, it can be found that TiNiFe alloys can obtain similar microstructures under the annealing processes of 823 K for 776 min, 827 K for 37 min, and 923 K for 12.5 min. And the recrystallization fractions are all around 50%. Nevertheless, the tensile properties and recovery stress of the alloys show almost similar values. And based on the feasibility of the annealing process, it is believed that annealing at 873 K for 37 min is the optimal choice to obtain a recrystallization fraction φR = 50%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.