Abstract
X-ray and ultraviolet photoelectron spectroscopies (XPS and UPS) were used to study epitaxial VN(001) layers grown in situ which were Ar+ sputter etched. The films were deposited on MgO(001) at 650 °C in pure N2 discharges maintained at a pressure of 5 mTorr (0.67 Pa) and shown to have a N/V ratio of 1.06 ± 0.02 by Rutherford backscattering (RBS). The films were sputter etched with 3 keV Ar+ at an angle of 40° to a constant nitrogen-to-vanadium ratio. A Mg Kα x-ray source was used to obtain the XPS data, while the UPS data was generated by He I and He II UV radiation. The sputter etched films were found to have a N/V ratio of 0.46, indicating a preferential removal of nitrogen.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.