Abstract
Alloy films of Co0.70Mn0.30 were grown on GaAs (001) substrates by molecular beam epitaxy at room temperature. The metastable tetragonally distorted single crystal structure was confirmed by reflection high energy electron diffraction and x-ray diffraction measurement, which exhibited a 2.87 Å in-plane lattice parameter. Ferromagnetic resonance measurements and theoretical fitting were performed and showed that, with a Mn capping layer, a uni-directional anisotropy existed. In addition, a fourfold tetragonal magnetocrystalline anisotropy as well as a uniaxial term in the film plane was also confirmed. The hysteresis loops recorded by longitudinal magneto-optical Kerr-effect also demonstrated the existence of different kinds of in-plane magnetic anisotropy. The origins of the anisotropy are explained tentatively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.