Abstract
We report on epitaxial growth and magnetic properties of Mn2.5Ga thin films, which were deposited on Cr/MgO single crystal substrates by magnetron sputtering. X-ray diffraction results revealed the epitaxial relationships as Mn2.5Ga(001)[100]∥Cr(001)[110]∥MgO(001)[100]. The presence of (002) and (011) superlattice peaks indicates that the films were crystallized into DO22 ordered structures. The perpendicular magnetic anisotropy (PMA) properties were found to be related to the extent of DO22 chemical ordering. A giant PMA (Kueff=1.2×107 erg/cm3) and low saturation magnetization (Ms=250 emu/cm3) can be obtained for the film with highest chemical ordering parameter (S=0.8).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.