Abstract
AbstractEpitaxial films of strontium bismuth tantalate (SrBi2Ta2O9, SBT) and strontium bismuth niobate (SrBi2Nb2O9, SBN) were grown using solution deposition techniques on magnesium oxide (MgO) substrates buffered with a 100 nm layer of lanthanum manganate (LaMnO3, LMO). Film structure and texture analyses were carried out using x-ray diffraction. Theta-2theta diffraction patterns were consistent with a c-axis aligned structure for both the buffer layer and the solution deposited films. Theta-2 theta scans revealed (001)SBT, SBN //(001) LMO epitaxial relationships between the solution deposited films and the buffer layer. A pole figure about the SBT, SBN (115) reflection indicated a single in-plane epitaxy. Film quality was assessed using ω and φ scans. Nuclear Magnetic Resonance (13C) was used to characterized the methoxy-ethoxide solutions used for the deposition of the SBN and SBT films.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.