Abstract
Abstract An investigation was carried out on API X60 steel specimens with surface cracks to study environmentally assisted crack growth rates in simulated groundwater (NS-4 solution). The environmental conditions were similar to those for buried natural gas pipelines in service, and loading was aggressive. The maximum stress intensity factor at the tip of the crack on the surface ranged from 20.6 MPa√m to 31.4 MPa√m. A periodic underload was applied to pre-cracked cantilever bending specimens. Tests were carried out for a period of 40 days at a frequency of either 1 cycle or 40 cycles per day. Crack growth rates were obtained for two stress ratios (R = minimum/maximum load) of 0 or 0.5 under both constant and variable amplitude loading conditions. Depending on loading conditions, the crack growth varied from 0 μm to 2,640 μm. However, the majority of crack growth measured was <100 μm. The experimental results showed that there was an acceleration in growth following an underload. The growth was higher whe...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.