Environmental application of millimeter-scale sponge iron (s-Fe0) particles (II): The effect of surface copper

Abstract

To enhance the catalytic reactivity of millimeter-scale particles of sponge iron (s-Fe0), Cu2+ ions were deposited on the surface of s-Fe0 using a simple direct reduction reaction, and the catalytic properties of the bimetallic system was tested for removal of rhodamine B (RhB) from an aqueous solution. The influence of Cu0 loading, catalyst dosage, particle size, initial RhB concentration, and initial pH were investigated, and the recyclability of the catalyst was also assessed.The results demonstrate that the 3∼5 millimeter s-Fe0 particles (s-Fe0(3∼5mm)) with 5wt% Cu loading gave the best results. The removal of RhB followed two-step, pseudo-first-order reaction kinetics. Cu0–s-Fe0 showed excellent stability after five reuse cycles. Cu0–s-Fe0 possesses great advantages compared to nanoscale zero-valent iron, iron power, and iron flakes as well as its bimetals. The surface Cu0 apparently catalyzes the production of reactive hydrogen atoms for indirect reaction and generates Fe-Cu galvanic cells that enhance electron transfer for direct reaction. This bimetallic catalyst shows great potential for the pre-treatment of recalcitrant wastewaters. Additionally, some oxides containing iron element are selected to simulate the adsorption process. The results prove that the adsorption process of FeOOH, Fe2O3 and Fe3O4 played minor role for the removal of RhB.