Enhancing Recovery of Ultra-Fine Magnetite from Low-Iron-Grade Cyanidation Tailings by Optimizing Flow Field Parameters of Low-Intensity Magnetic Separation (LIMS)

Abstract

The characteristics of iron minerals in cyanidation tailings with a low iron grade were determined via chemical composition analysis, iron phase analysis, and mineral liberation analysis (MLA). The results showed that the cyanidation tailings contained 15.68% iron, mainly occurring in the form of magnetite (19.66%) and limonite (79.91%), in which 16.52% magnetite and 65.90% limonite particles were fully liberated. Most ultra-fine magnetite grains were adjacent and wrapped with limonite to form complex intergrowths, which resulted in low-efficiency magnetite recovery in low-intensity magnetic separation (LIMS) and adversely affected the downstream high-gradient magnetic separation (HGMS) process. Thus, in this work, the optimization of the flow field was proposed to enhance the separation of ultra-fine magnetite from the cyanidation tailings using pilot-scale LIMS separation, and the controllable parameters (including feed flow, separation gap, drum rotating speed, and solid weight) affecting ultra-fine magnetite capture were investigated. Under optimized conditions, a high-grade magnetite concentrate assaying 63.31% Fe with 86.46% magnetite recovery was produced, which, respectively, increased by 0.76% and 15.22%, compared with those obtained from industrial production. In addition, from the flow dynamics simulation, it was found that the magnetite particles in the −6 µm ultra-fine fraction were lost much more easily than those of coarser fractions due to the relatively enhanced hydrodynamic drag force acting on the particles compared with the magnetic force. However, this loss would be effectively reduced with the regulation and control of the flow field. The iron recoveries in the −16~+6 µm and −6 µm fractions of magnetite concentrate increased by 3.66% and 4.42%, respectively, under optimized hydrodynamic conditions. This research outcome provides a valuable reference for the economic and effective utilization of iron resources from such solid wastes.