Abstract
Lead free perovskite (Ba1-xCax)TiO3 (BCT) (0 < x ≤ 0.4) ceramics were successfully prepared by Sol gel technique in lower thermal processing conditions than the solid solution method. The samples were calcined at 1000 °C/and they were sintered at 1200 °C. The structure, dielectric, leakage current and ferro-piezoelectric properties of perovskite (Ba1-xCax)TiO3 (0 < x < 0.4) were investigated. In Ca-doping range 0 < x < 0.3, pure single phase of BCT has been detected. Secondary phase of CaTiO3 has been detected for x = 0.4. The addition of Ca2+ has a negligible effect on the Curie temperature but it inhibits the grain dwindle. High permittivity and low dielectric loss values were achieved in the sample (Ba0.8Ca0.2)TiO3 due to Morphotropic Phase Boundary (MPB) coexistence. Anomalous switching leakage peak (∼2 kV/cm) was observed due to the domain switching. The (Ba0.8Ca0.2)TiO3 exhibits low leakage even in the absence of the electric field (Joff = 1.5368e−13 A/cm2), due to the enhancement of the microstructure properties. The Ferroelectric properties were estimated by P-E loop and Positive Up Negative Down (PUND) methods and the results are shown the remnant polarization estimated by P-E loop is almost back to leakage current contribution. Piezoelectric properties were enhanced in (Ba0.8Ca0.2)TiO3 (d∗33 = 498 pm/v) due to BT-CT phases coexistence.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.