Abstract
The effects of substituting Fe with Ni on thermal properties, glass-forming ability (GFA) and magnetic properties of Fe76-xNixMo3.5P10C4B4Si2.5 (x = 0−30 at.%) alloys were investigated in detail. The breadth of the supercooled liquid region was found to gradually increase from 42 to 55 K with increasing Ni content to 30 at.%. When x = 5 at.%, the alloy composition approached a eutectic point, resulting in an increase in GFA. As a result, FeNiMoPCBSi bulk metallic glasses with critical diameters up to 5.5 mm were successfully synthesized by copper mold casting. These glassy alloys exhibit a high saturation magnetic flux density of 0.75−1.21 T and excellent soft magnetic properties, i.e., low coercive force of 1.1−2.0 A/m, and high effective permeability of 14400−19700 at 1 kHz under a field of 1 A/m. The reasons for the high stability of the supercooled liquid, and the high GFA as well as excellent soft magnetic properties are discussed in this article.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.