Abstract
We investigated the tunability of the transport and magnetic properties in 7.5nm La0.7Sr0.3MnO3 (LSMO) epitaxial films in a field effect geometry with the ferroelectric copolymer P(VDF-TrFE) as the gate insulator. Two different switching behaviors were observed upon application of gate voltages with either high or low magnitudes. The application of single voltage pulses of alternating polarity with an amplitude high enough to switch the remanent polarization of the ferroelectric copolymer led to a 15% change of the resistance of the LSMO channel at temperature 300K (but less than 1% change at 20K). A minimal shift of the peak in the resistance-temperature plot was observed, implying that the Curie temperature TC of the manganite layer is not changed. Alternatively, the application of a chain of low voltage pulses was found to shift TC by more than 16K, and a change of the channel resistance by a 45% was obtained. We attribute this effect to the field-assisted injection and removal of oxygen vacancies in the LSMO layer, which can occur across the thickness of the oxide film. By controlling the oxygen migration, the low-field switching route offers a simple method for modulating the electric and magnetic properties of manganite films.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.