Enhanced transport properties of graphene oxide based cement composite material

Abstract

This study is aimed to evaluate the transport properties of a cement composite incorporated with graphene oxide (GO). GO is a 2-dimensional nano material, enriched with reactive oxygen functional groups which made it as a suitable reactive material with cementitious materials. The GO-cement composite was prepared by adding GO in four different proportions such as 0.01%, 0.02%, 0.03%, and 0.04% by weight of cement. In the durability aspect water absorption, water sorptivity, resistance to acid attack, mechanical properties, thermal analysis, chloride migration coefficient, and chloride penetration depth were examined experimentally for GO-cement composite specimens and compared with plane cement composite specimens. Experimental results indicated that 14.5%, 30%, and 40.47% degradation in water absorption capacity, chloride migration coefficient, and chloride penetration depth of cement composite specimens with 0.03% addition of graphene oxide than normal cement composite specimens at 28 days of curing. Additionally, significant decrement in the sorptivity coefficient of cement composite was also achieved at 0.03% of GO addition. Mechanical properties were enhanced by 77.70% in flexural strength at 0.03% of GO addition and 47.61% in compressive strength at 0.04% of GO addition in cement composite at 28 days of curing. SEM analysis of the test samples exhibited the pore filled structure of the cement composites with GO addition. In addition, all GO-cement composite specimens exhibited greater resistance to an acidic environment and negligible loss in strength and weight was observed than normal cement composite specimens at 28 days immersion in 2% and 5% concentrations of both H2SO4 and HCl acidic solutions. Thermal resistance was increased in the terms of compressive strength in all GO-cement composite mixes gradually by increasing the concentration of GO content from 0.01% to 0.04% by weight of cement. It can be concluded that an effective improvement in transport properties of cement composite was achieved by the incorporation of graphene oxide nano material.