Abstract
The effect of a thin RuOx layer formed on the Ru/TiN/doped poly-Si/Si stack structure was compared with that on the RuOx/TiN/doped poly-Si/Si stack structure over the post-deposition annealing temperature ranges of 450–600°C. The Ru/TiN/poly-Si/Si contact system exhibited linear behavior at forward bias with a small increase in the total resistance up to 600°C. The RuOx/TiN/poly-Si/Si contact system exhibited nonlinear characteristics under forward bias at 450°C, which is attributed to no formation of a thin RuOx layer at the RuOx surface and porous-amorphous microstructure. In the former case, the addition of oxygen at the surface layer of the Ru film by pre-annealing leads to the formation of a thin RuOx layer and chemically strong Ru-O bonds. This results from the retardation of oxygen diffusion caused by the discontinuity of diffusion paths. In particular, the RuOx layer in a nonstoichiometric state is changed to the RuO2-crystalline phase in a stoichiometric state after post-deposition annealing; this phase can act as an oxygen-capture layer. Therefore, it appears that the electrical properties of the Ru/TiN/poly-Si/Si contact system are better than those of the RuOx/TiN/poly-Si/Si contact system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.