Abstract
Using directional solidification technique, a series of Nb–Si in situ composites with nominal compositions of Nb–16Si–23Ti–4Cr–2Al-2Hf-xRe (x = 0, 0.1, 0.4, 0.6, at.%) were manufactured to investigate the phase constituent, microstructural evolution and room temperature fracture toughness. These four different alloys all consisted of Nbss, αNb5Si3 and γNb5Si3, while Rhenium was primarily partitioned in Nbss matrix. With further addition content of Re, the silicide got refinement firstly, its average size minimized to 4.68 μm in 0.4Re alloy; but that coarsened again in 0.6Re alloy which resulting in the maximum micro-hardness of 1627 HV. The ductile Nbss matrix in 0.4Re alloy exhibited best continuity and its volume fraction rose to 63.1%; that triggered more obvious microcrack, fracture step and crack bifurcation, especially interface decohesion during loading process, thus increasing the room temperature fracture toughness from 8.4 MPa m1/2 to 13.1 MPa m1/2. But the 0.6Re alloy had an adverse effect on room temperature plasticity due to higher proportion and larger size of silicide, then exerted perceptible constraint for ductile Nbss matrix. In order to better optimize the mechanical performance of Nb–Si based alloys, the alloying amount of Rhenium should be properly selected to circumvent its concentration-sensitive effect.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.