Abstract
Bulk oxygenated amorphous carbon films (a-C:H:O) with different oxygen concentrations are deposited on high-speed steel with a chromium carbide (CrCx) interlayer using an anode layer ion source (ALIS) and their structural, mechanical, and tribological properties are determined. Films with 7 at%, 9 at%, 13 at%, and 27 at % oxygen are prepared by changing the O2 to C2H2 ratio in the gas mixture during deposition. The film deposited without intentionally introducing oxygen has an oxygen concentration of 5% and serves as the control sample. The surface of the control film contains nanodots which can be reduced with 10% O2 in the gas mixture. The best properties are obtained from the film containing 7 at% oxygen. The hardness increases from 19.5 GPa for the control film to 29.0 GPa of the a-C:H:O film with 7 at% oxygen. At the same time, the wear rate decreases by 2.5 times to 2.0 × 10−7 mm3/m-N and the friction coefficient by 10 times to 0.09. If the oxygen concentration in the film exceeds 7%, the hardness begins to decrease and wear rate increases while the friction coefficient is reduced slightly. Raman scattering reveals a smaller ID/IG ratio and more disorder in the 7% sample and XPS shows that the improvement stems from increased sp3 hybridization and C–C bonding. However, if the oxygen concentration in the gas mixture is increased further, oxygen ions begin to replace carbon atoms in the sp3 structure and more O–C–O, CO, and O–CO bonds are created. The carbonyl and carboxylic groups soften the matrix and degrade the mechanical properties. Our results clarify the effects and mechanism of oxygen on the mechanical and tribological properties of bulk amorphous carbon films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.