Abstract
Fe36Co36B19.2Si4.8Nb4 bulk glassy rods were synthesized by copper mould casting. The effects of annealing treatments on the microstructure, elastic and mechanical properties of this alloy are investigated. Annealing below the glass transition temperature induces the formation of atomic clusters with pseudo-tenfold symmetry with a close relationship to the Fe23B6 phase. Annealing at sufficiently high temperatures promotes the formation of stable Fe2B and FeB phases and Fe(Co) solid solution. The as-cast alloy exhibits ultra-high hardness (H>14GPa), high reduced Young’s modulus (Er>200GPa) and good wear resistance. These properties are further enhanced after thermal treatments (H>18GPa and Er>260GPa are achieved in the fully crystallized sample). The mechanical hardening is accompanied with an increase of the elastic recovery and a decrease of the Poisson’s ratio. The different microstructural mechanisms responsible for these annealing-induced changes in mechanical and elastic properties are discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.