Abstract
The diamond thick layers prepared using chemical vapor deposition (CVD) methods have been treated at high pressures and high temperatures (HP-HT). It was found that the Vickers hardness of the HP-HT treated bulks was nearly two times as high as that of the starting CVD diamond samples. The hardness of the samples treated at 8 GPa and 1800°C is ∼80 GPa at a loading force of 49 N, close to that of the single-crystal diamond (∼100 GPa). In addition, the oxidation resistance of CVD diamond samples was also enhanced greatly after HP-HT treatments, and the diamondization of sp2 bonded carbon in the CVD diamond samples could occur at 7–8 GPa and 1600–1800°C. The HP-HT conditions of diamondization in our works are much lower than the case of the graphite-to-diamond direct transformation without the presence of catalyst (>15 GPa and 2000°C).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.