Mn55Bi45 melt - spun ribbons were prepared by using the melt-spinning technique followed by annealing in Ar/5%H2 gas mixture. The in-situ formation of ferromagnetic phase (denoted as LTP) of MnBi was observed by the multi-section cycled Differential Scanning Calorimetry (DSC) method. It was found that, the optimal annealing temperature range for forming MnBi LTP is 250 – 280 oC. The prolonging annealing time increases the content of MnBi LTP leading to the increase of saturation magnetization Ms but paid by the drop of the intrinsic coercivity iHc. The MnBi green powders were prepared by the Low Energy Ball Milling method (LEBM) in N2 liquid. The maximum energy product of MnBi green powders is estimated about 10.8 MGOe.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.