Abstract
We, respectively, fabricated GdBa2Cu3O7−δ (Gd123) single domain superconductors by melt growth process in air with Gd2Ba4CuZrOx (GdZr2411) and nanosize ZrO2 dopants. The microstructures and superconducting properties were investigated by scanning/transmission electron microscopy (SEM/TEM) and SQUID. GdZr2411 and BaZrO3 particles with the average size of 50nm were observed in the GdZr2411 and nanosize ZrO2 doped Gd123 bulks by TEM, respectively. Critical current density (Jc) was enhanced up to 100,000A/cm2 at 77K and self-field with 0.4mol% nano-sized ZrO2. The present study also showed that small amount GdZr2411 dopants (8mol%, ratio to Gd123) were effective to induce a δTc-type pinning.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.