Abstract
Lead-free (1-x)Ba0.8Sr0.2TiO3-xBiTaO3 (BST-xBTA) ceramics were prepared via a solid-state reaction process. The effect of BTA addition on the energy storage properties of BST ceramics was investigated. The pure perovskite phases were found in the BST-xBTA ceramic samples as x ≤ 0.12. With the increasing BTA content, the maximum breakdown strength (Eb) reached 130 kV/cm at x = 0.12, twice that of the undoped samples. The large Eb and slim ferroelectric loops of the 0.88BST-0.12BTA ceramics indicated an advantageous energy density of Wrec ∼0.526 J/cm3 and a high energy efficiency of η ∼98% at 130 kV/cm. The low dielectric loss and high η make this ceramic system a promising material applying pulsed-powder devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.