Abstract
Niobium alloys play an indispensable role in aerospace technology. However, traditional niobium alloys has unsatisfactory or high-temperature strength or limited room-temperature. This work introduces Nb2MoxWyC0.25 alloys with strength-plasticity balance by optimizing refractory alloy elements and eutectic carbides drawing on the design concepts of eutectic high-entropy alloys. The influence of Mo and W contents on the microstructure and mechanical properties of the alloys was studied. The Nb2MoxWyC0.25 alloy contain body-centered cubic (BCC) primary phase and eutectic structures composed of BCC and carbide phases with semi-coherent interfaces. Appropriate additions of Mo and W refine the grain size of the primary BCC phase and cause the carbide phase to evolve from Nb2C to NbC. The Nb2Mo0.5W0.5C0.25 hypoeutectic niobium alloy composed of BCC and Nb2C phases with a relatively small lattice mismatch has a room-temperature yield strength of 1.27 ± 0.04 GPa, compressive strength of 2.03 ± 0.06 GPa, and a fracture strain of 17.8 ± 2.2 %. Solid solution strengthening in the BCC phase and second-phase strengthening of the carbide phase simultaneously enhance the alloy. The fine grain strengthening, reduced crack origination at low mismatch interface, and the crack tip by soft BCC at the phase interface improve the plasticity simultaneously. This paper provides a method to improve the room-temperature plasticity and strength of refractory niobium alloys, laying the foundation for the industrial application of refractory niobium alloys.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call